   A Comparative Study of Insulators on Magnetic Properties of Sendust Based Nanocomposite Powder Cores  
   
نویسنده Amoohadi Maryam ,Mozaffari Morteza ,Gharaati Abdolrasoul ,Rezazadeh Mohammad
منبع Journal Of Optoelectronical Nanostructures - 2018 - دوره : 3 - شماره : 4 - صفحه:1 -14
چکیده    In this study, sendust (fe85si9.6al5.4) nanostructure alloy was prepared by mechanical alloying and was characterized by x-ray diffraction. in addition, the alloy’s morphology and its distribution particle size were investigated by scanning electron microscopy method. the alloyed powders were insulated with 4wt% of three different insulating materials including polyvinyl alcohol, epoxy resin, and sodium silicate. then, 0.5 wt% zinc stearate was added as a lubricant and the composites were formed at a pressure of 1600 mpa in a torodial die. these cores were annealed in ar atmosphere at 350 to 450 ºc for 1 h. some of the magnetic parameters of the as-milled and annealed samples were measured and compared with each other in the frequency range of 4 to 1000 khz. the results showed that polyvinyl alcohol is not a suitable insulating agent for insulating this alloy. in addition, the real part of the initial magnetic permeability of the magnetic powder core insulated by sodium silicate in comparison with that insulated by epoxy resin is a bit smaller, but more reduction of the imaginary part of former results in an increase the q-factor throughout measuring frequency range. the results show that annealing is more effective on improvement of the measured magnetic properties of the samples insulated with sodium silicate than that insulated with epoxy resin.
کلیدواژه Soft Magnetic Composite Powder Cores ,Epoxy Resin Insulator ,Sodium Silicate Insulator ,Magnetic Permeability ,Q-Factor
آدرس Payamenoor University, Department Of Physics, ایران, University Of Isfahan, Faculty Of Science, Department Of Physics, ایران, Payamenoor University, Department Of Physics, ایران, Isfahan University Of Technology, Department Of Materials Engineering, ایران
پست الکترونیکی rezazadeh.moh@gmail.com
 
 

Copyright 2023
Islamic World Science Citation Center
All Rights Reserved